高爐、熱風爐用低蠕變高鋁磚系我廠采用優質高鋁礬土，添加抗蠕變改性材料經高壓成型高溫燒成生產的適用于高爐、熱風爐爐膛內襯的低蠕變耐火材料。
Low creep high-alumina brick whose raw material is excellent high-alumina bauxite and anti-creep modified material is produced by means of high pressure formation and high temperature burning , which can be used as low creep refractory of the inner lining of blast furnace and hot-blast stove .

指標/牌號	低蠕變高鋁磚			復合莫來石磚	堇青石磚	低蠕變粘土磚		致密粘土磚
指標/牌號	H-HD	H-HL	H-LL	H-LLG	H-JL	H-HN	H-LN	H-VN
Al₂O₃ %	80±5	75±5	65±5	65±5	55±5	42±5	40±5	42±5
Fe₂O₃ %	≤1.5	≤1.5	≤1.5	≤1.0	≤1.5	≤1.5	≤2.0	≤1.5
MgO %						≤2.0
顯氣孔率 %	≤21	≤20	≤21	≤20	≤25	≤22	≤24	≤16
體積密度 g/cm³	2.7	2.7	2.6	2.6	2.3	2.2	2.1	2.3
常溫耐壓強度Mpa	≥55	≥60	≥55	≥70	≥40	≥40	≥30	≥45
耐火度℃	≥1850	≥1790	≥1790	≥1790		≥1750	≥1730	≥1750
荷重軟化溫度0.2Mpa ℃		≥1600	≥1600	≥1600	≥1400	≥1400	≥1350	≥1400
蠕變率%(50h)	1500℃≤0.8	1400℃≤0.6	1300℃≤0.8			1200℃≤1.0	1100℃≤1.0
熱震穩定性次數	≥6	≥6	≥25	1200℃≥20
熱膨脹率%			1300℃≤0.8
重燒線變化率%2h		1500℃ ±0.1	1500℃ ±0.1		1450℃ ±0.2	1450℃ 0-0.4	1450℃ 0-0.3	1450℃ 0-0.4

已閱：968次發布時間：2024-05-22